棕刚玉段砂
棕刚玉以优质铝矾土为原料，无烟煤，铁霄，在电弧中经2000度以上高温熔炼制成，经自磨机粉碎 整形，磁选去铁，筛分成多种粒度，其质地致密、硬度高，粒形成球状，适用于制造陶 瓷、树脂高固结磨具以及研磨、抛光、喷砂、精密铸造等，还可用于制造高级耐火材料 。
棕刚玉段砂 0-1mm 1-3mm 3-5mm 5-8mm
Al2O3 | Fe2O3 | TiO2 | SiO2 | K2O | CaO | Na2O |
95.0% | ≤0.35% | 1.7-3.4% | ≤1.5% | ≤0.01% | / | / |
物理特性
莫氏硬度 | 比重 | 堆积密度 | PH值 | 耐火度 |
9.0 | ≥3.90g/cm3 | 1.75-1.95g/cm3 | 7.0 | 2100℃ |
粒度组成标准GB/T 2478-2008
粒度 | 单位 | 保证值 | 典型值 | |||||||
8-5mm | mm | +8.00 | -4.00 | +9.52 | +8.00 | +6.70 | +5.60 | +4.75 | -4.00 | - |
% | 5 | 5 | 0 | 0-5 | 35-55 | 75-95 | 90-100 | 0-5 | ||
6-3mm | mm | +5.60 | -2.80 | +8.00 | +6.70 | +5.60 | +4.75 | +3.35 | +2.80 | -2.80 |
% | ≤40 | ≤10 | 0 | 0-5 | 15-35 | 40-65 | 75-95 | 90-100 | 0-10 | |
5-3mm | mm | +4.75 | -2.80 | +5.6 | +4.75 | +3.35 | +2.80 | -2.80 | ||
% | ≤10 | ≤10 | 0 | 0-10 | 60-80 | 90-100 | 0-10 | |||
3-1mm | mm | +2.80 | -1.0 | +4.75 | +3.35 | +2.80 | +2.00 | +1.18 | +1.00 | -1.00 |
% | ≤10 | ≤10 | 0 | 0-5 | 1-10 | 30-50 | 70-90 | 90-100 | 0-10 | |
1-0mm | mm | +1.00 | -0.212 | +1.18 | +1.00 | +0.50 | +0.212 | -0.212 | ||
% | ≤10 | ≤35 | 0 | 0-5 | 30-50 | 65-85 | 0-35 | |||
包装25公斤袋装/散吨包
主要用途：不定型耐火材料 ，定型耐火材料，浇注料， 钢包用耐火材料 ， 高炉热风炉用系列组合砖 ， 高铝砖 ， 含碳耐材 ， 莫来石砖 ， 炮泥 ， 喷枪 ， 散装料 ， 陶瓷杯 ， 粘土砖 ， 组合砖 ，刚玉制品，陶瓷过滤板等